This study investigated the softening mechanisms of the AISI 410 martensitic stainless steel during torsion simulation under isothermal continuous in the temperature range of 900 to 1150 °C and strain rates of 0.1 to 5.0s-1. In the first part of the curves, before the peak, the results show that the critical (εc) and peak (εp) strains are elevated for higher strain rate and lower temperatures contributing for higher strain hardening rate (h). Moreover, this indicated that dynamic recrystallization (DRX) and dynamic recovery (DRV) are not effective in this region. After the peak, the reductions in stresses are associated to the different DRX/DRV competitions. For lower temperatures and higher strain rates there is a delay in the DRX while the DRV is acting predominantly (with low Avrami exponent (n) and high t0.5). The steady state was reached after large strains showing DRX grains, formation of retained austenite and the presence of chromium carbide (Cr23C6) and ferrite δ at the martensitic grain boundaries. These contribute for impairing the toughness and ductility on the material. The constitutive equations at the peak strain indicated changes in the deformation mechanism, with variable strain rate sensitivity (m), which affected the final microstructure.

The aim of this work is evaluate the influence of welding conditions on abrasive wear resistance in coating of Fe-Cr-C. The metal base used in this investigation was the steel SAE 1020 and as welded metal the selfshilded tubular wires of Fe-Cr-C with 1.6 mm of diameter. The welding parameter such as amperage, voltage, welding speed, wire feed speed and the distance between the point and samples were kept constant by varying the electrode inclination and the number of layers deposited. These resulted in four different weld conditions: pulling and pushing the weld pool and hardfacing formed with 1 end 2 layers. Their influences on dilution, microhardness and microstructure were evaluated and correlated with the abrasive wear according to the standard tests methods for abrasion measurements through the usage of dry sand/rubber wheel apparatus, ASTM G-65-04. The results showed that the wear resistance of the four different conditions was affected by dilution, microstructure morphology and carbide volume fraction. The best conditions for hardfacing deposition were for pushing the torch and two layers added.

An austenitic stainless steel ISO 5832-9 used as a biomaterial was torsion-deformed over the temperature range of 1000-1200 °C and strain rates of 0.05, 0.1, 1.0 and 5.0 s- 1. The flow stress curves obtained showed two regions where firstly there is a rising on stress characterized as work hardening mechanism acting and secondly a decreasing in work-softening after a peak stress. The flow curves were modeled by adjusting the experimental data with Zener-Hollomom parameter to construct the constitutive equations that describe the plastic behavior in both regions. The first region was described until the peak stress, taking into consideration the competition between work hardening and recovery while the second one was described applying the softening time of 50% and the Avrami equation. In some hot deformation conditions the simulated curves showed good agreement with the experimental ones while in others conditions the simulated showed differences to experimental curves that was discussed and associated with other mechanisms that acted during hot deformation.